Alloy (ISS) |
Equivalent alloy (A.A) |
Copper |
Magnesium |
Silicon | Iron | Managanese Others* (Total) | Remarks | ||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Old | New |
U.S.A |
Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Max | Max. | Aluminum 99.0% Min. | ||
| 1 B | 19500 | 1050 | — | 0.05 | — | — | — | 0.30 | 0.4 | — | 0.05 | 0.1 | Aluminum 99.5% Min. | ||
| Aluminium 1060 | Fe | Si | Mg | Mn | Cu | Zn | Ti | Al |
| 0.15 - 0.20 | 0.10 - 0.15 | 0.01 - 0.03 | 0.01 - 0.03 | 0.01 - 0.05 | 0.01 - 0.03 | 0.020 - 0.030 | 99.60 |
| Aluminium 1070 | Fe | Si | Mg | Mn | Cu | Zn | Ti | Al |
| 0.25 | 0.2 | 0.03 | 0.03 | 0.03 | 0.07 | 0.03 | 99.70 |
| Alloy | Fe | Si | Mg | Mn | Cu | Zn | Ti | Cr | Others | AI |
| 1100 (min) | 0.35 | 0.25 | 0.01 | 0.01 | 0.05 | 0.01 | 0.020 | Trace | 0.05 (each) | 99.60% |
| 1100 (max) | 0.50 | 0.35 | 0.03 | 0.05 | 0.20 | 0.05 | 0.030 | Trace | 0.15 (total) | remainder |
| Alloy | Si | Fe | Cu | Zn | Mn | Mg | Ti | Other | Cr | Ni | Others | Ti+Zr | Al |
| 2014 (min) (max) | 0.50 - 0.90 | 0.0 - 0.50 | 3.90 - 5.00 | 0.0 - 0.25 | 0.40 - 1.20 | 0.20 - 0.80 | 0.0 - 0.15 | 0.0 - 0.15 | 0.0 - 0.10 | 0.0 - 0.10 | 0.0 - 0.05 | 0.0 - 0.20 | Balance |
| Al | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Other Each | Other Total |
| Bal. | 0.20-0.8 | 0.7 max | 3.5-4.5 | 0.40-1.0 | 0.40-0.8 | 0.10 max | 0.25 max | 0.15 max | 0.05 max | 0.15 max |
| Al | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Other | |
| min. | Bal | 3.80 | 0.30 | 1.20 | ||||||
| max. | Bal | 0.50 | 0.50 | 4.90 | 0.90 | 1.80 | 0.10 | 0.25 | 0.15 | 0.05 |
| Al | Cr | Cu | Fe | Mg | Mn | Other Total | Si | Ti | Zn |
| Remainder | - | 0.05 to 0.20% | 0.7% | - | 1.0 to 1.5% | 0.15% | 0.6% | - | 0.10% |
| Element | % | Element | % |
| Aluminium | Balance | Manganese | 0.20 max |
| Magnesium | 0.50 – 1.10 | Chromium | 0.10 max |
| Silicon | 0.30max | Zinc | 0.25 max |
| Iron | 0.07 max | Others, each | 0.05 max |
| Copper | 0.20 max | Others, total | 0.15 max |
| Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Al |
| 0.50 | 0.50 | 3.8/4.9 | 0.30/0.9 | 1.2/1.8 | 0.10 | 0.25 | 0.15 | Balance |
| Mg | Mn | Si | Cu | Fe | Cr | Zn | Ti | Cu | Other (Each) | Others (Total) | Al |
| 2.60 - 3.60 | 0.0 - 0.50 | 0.0 - 0.40 | 0.0 - 0.40 | 0.0 - 0.30 | 0.0 - 0.20 | 0.0 - 0.15 | 0.0 - 0.10 | 0.0 - 0.05 | 0.0 - 0.05 | 0.0 - 0.15 | Balance |
| Al | Si | Fe | Cu | Mn | Cr | Mg | Ti | Zn | Other Each | Others Total |
| Bal | 0.40 max | 0.40 max | 0.10 max | 0.40 / 1.0 | 0.05 / 0.25 | 4.0 / 4.90 | 0.15 max | 0.25 max | 0.05 max | 0.15 max |
| Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Others, each | Others, total | Al |
| 0.4 | 0.5 | 0.1 | 0.20-0.70 | 3.5-4.5 | 0.05-0.25 | 0.25 | 0.15 | 0.05 | 0.15 | Balance |
| Mn | Si | Cr | Cu | Fe | Zn | Al | Mg | Ti | Other Each/Total |
| 0.15 | 0.4-0.8 | 0.15-0.35 | 0.15-0.4 | 0.7 | 0.25 | Remainder | 0.8-1.2 | 0.15 | 0.005/0.15 |
| Weight % | Zn | Cu | Mg | Zr | Fe | Si | Mn | Ti | Cr | Others(total) |
| Minimum | 5.7 | 2.0 | 1.9 | 0.08 | - | - | - | - | - | - |
| Maximum | 6.7 | 2.6 | 2.6 | 0.15 | 0.15 | 0.12 | 0.10 | 0.06 | 0.04 | 0.15 |
| Weight % | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Each | Total |
| Minimum | 1.20 | 2.10 | 0.18 | 5.10 | ||||||
| Maximum | 0.40 | 0.50 | 2.00 | 0.30 | 2.90 | 0.28 | 6.10 | 0.20 | 0.05 | 0.15 |
| Alloy | Equivalent alloy (A.A) | Si | Fe | Cu | Zn | Mn | Mg | Ti | Cr | Others | AI | |||||||||||
| Old | New |
U.S.A |
Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | ||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| H15 | 24345 | 2014 | 0.50 | 0.90 | 0.0 | 0.50 | 3.90 | 5.00 | 0.00 | 0.25 | 0.40 | 1.20 | 0.20 | 0.80 | 0.0 | 0.15 | 0.0 | 0.10 | 0.0 (each) | 0.05 (total) | balance | |
| Alloy | Equivalent alloy (A.A) | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Other each | Other total | AI | ||||||||||||
| Old | New |
U.S.A |
Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | ||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| H14 | 24534 | 2017 | 0.20 | 0.8 | - | 0.7 | 3.5 | 4.5 | 0.40 | 1.0 | 0.40 | 0.8 | - | 0.10 | - | 0.25 | - | 0.15 | - | 0.05 | - | 0.15 | bal | |
| Alloy | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Other | AI | ||||||||||
| 2024 | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| - | 0.50 | - | 0.50 | 3.80 | 4.90 | 0.30 | 0.90 | 1.20 | 1.80 | - | 0.10 | - | 0.25 | - | 0.15 | - | 0.05 | bal | bal | |
| Alloy | Fe | Si | Mg | Mn | Cu | Zn | Ti | Al |
| 5083 | 0.4 | 0.4 | 4.0-4.9 | 0.4-1.0 | 0.1 | 0.25 | 0.15 | Bal |
|---|
| Alloy | Mn | Si | Cr | Cu | Fe | Zn | Al | Mg | Ti | Other Each/Total |
| 6061 | 0.15 | 0.4-0.8 | 0.15-0.35 | 0.15-0.4 | 0.7 | 0.25 | Remainder | 0.8-1.2 | 0.15 | 0.005/0.15 |
|---|
| Alloy | Cu | Si | Fe | Mn | Mg | Zn | Cr | Ti | Other Each | Others Total | Al |
| 6063 | .10 (max) | .20/.60 | .35 (max) | .10 (max) | .45/.90 | .10 (max) | .10 (max) | .10 (max) | .05 | .015 | Remainder |
|---|
| Alloy | Al | Si | Fe | Cu | Mn | Cr | Mg | Zn | Ti | Other Each | Others Total |
| Aluminium 6082 | Bal | 0.7 - 1.3 | 0.50 max | 0.10 max | 0.40-1.00 | 0.25 max | 0.06-1.20 | 0.20 max | 0.10 max | 0.05 max | 0.15 max |
| Alloy | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Each | Total |
Aluminium 7075 |
Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| - | 0.40 | - | 0.50 | 1.20 | 2.00 | - | 0.30 | 2.10 | 2.90 | 0.18 | 0.28 | 5.10 | 6.10 | - | 0.20 | - | 0.05 | - | 0.15 | |
| Aluminium 2014 | Fe | Si | Mg | Mn | Cu | Zn | Ti | Al |
| 0.7 | 0.50 - 1.20 | 0.2 - 0.8 | 0.4 - 1.2 | 3.9 - 5.0 | 0.25 | 0.15 | 93.5 |
| Grade | Al | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Others Each | Other Total |
| 2017 | Rem | 0.20-0.8 | 0.7 max | 3.5-4.5 | 0.40-1.0 | 0.40-0.8 | 0.10 max | 0.25 max | 0.15 max | 0.05 max | 0.15 max |
| Grade | Al | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Other |
| min. | Bal | 3.80 | 0.30 | 1.20 | ||||||
| max. | Bal | 0.50 | 0.50 | 4.90 | 0.90 | 1.80 | 0.10 | 0.25 | 0.15 | 0.05 |
| Weight% | Al | Si | Fe | Cu | Mn | Cr | Mg | Ti | Zn | Other Each | Others Total |
| 5083 | Bal | 0.40 max | 0.40 max | 0.10 max | 0.40 / 1.0 | 0.05 / 0.25 | 4.0 / 4.90 | 0.15 max | 0.25 max | 0.05 max | 0.15 max |
| Mn | Si | Cr | Cu | Fe | Zn | Al | Mg | Ti | Other Each/Total |
| 0.15 | 0.4-0.8 | 0.15-0.35 | 0.15-0.4 | 0.7 | 0.25 | Remainder | 0.8-1.2 | 0.15 | 0.005/0.15 |
| Cu | Si | Fe | Mn | Mg | Zn | Cr | Ti | Other Each | Others Total | Al |
| .10 (max) | .20/.60 | .35 (max) | .10 (max) | .45/.90 | .10 (max) | .10 (max) | .10 (max) | .05 | .015 | Remainder |
| Weight% | Al | Si | Fe | Cu | Mn | Cr | Mg | Zn | Ti | Other Each | Others Total |
| Aluminium 6082 | Bal | 0.7 - 1.3 | 0.50 max | 0.10 max | 0.40-1.00 | 0.25 max | 0.06-1.20 | 0.20 max | 0.10 max | 0.05 max | 0.15 max |
| Weight % | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Each | Total |
| Minimum | 1.20 | 2.10 | 0.18 | 5.10 | ||||||
| Maximum | 0.40 | 0.50 | 2.00 | 0.30 | 2.90 | 0.28 | 6.10 | 0.20 | 0.05 | 0.15 |
| Aluminium 2014 | Fe | Si | Mg | Mn | Cu | Zn | Ti | Al |
| 0.7 | 0.50 - 1.20 | 0.2 - 0.8 | 0.4 - 1.2 | 3.9 - 5.0 | 0.25 | 0.15 | 93.5 |
| Grade | Al | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Other |
| min. | Bal | 3.80 | 0.30 | 1.20 | ||||||
| max. | Bal | 0.50 | 0.50 | 4.90 | 0.90 | 1.80 | 0.10 | 0.25 | 0.15 | 0.05 |
| Weight% | Al | Si | Fe | Cu | Mn | Cr | Mg | Ti | Zn | Other Each | Others Total |
| 5083 | Bal | 0.40 max | 0.40 max | 0.10 max | 0.40 / 1.0 | 0.05 / 0.25 | 4.0 / 4.90 | 0.15 max | 0.25 max | 0.05 max | 0.15 max |
| Mn | Si | Cr | Cu | Fe | Zn | Al | Mg | Ti | Other Each/Total |
| 0.15 | 0.4-0.8 | 0.15-0.35 | 0.15-0.4 | 0.7 | 0.25 | Remainder | 0.8-1.2 | 0.15 | 0.005/0.15 |
| Cu | Si | Fe | Mn | Mg | Zn | Cr | Ti | Other Each | Others Total | Al |
| .10 (max) | .20/.60 | .35 (max) | .10 (max) | .45/.90 | .10 (max) | .10 (max) | .10 (max) | .05 | .015 | Remainder |
| Weight% | Al | Si | Fe | Cu | Mn | Cr | Mg | Zn | Ti | Other Each | Others Total |
| Aluminium 6082 | Bal | 0.7 - 1.3 | 0.50 max | 0.10 max | 0.40-1.00 | 0.25 max | 0.06-1.20 | 0.20 max | 0.10 max | 0.05 max | 0.15 max |
| Alloy | Temper | UTS (Mpa) | Yield Strength (Mpa) | Elongation (%) | ||
|---|---|---|---|---|---|---|
| Minimum | Maximum | Minimum | Maximum | A 50mm (Minimum) | ||
| EN AW-1050 A | F | 60 | – | 20 | – | 23 |
| O | 60 | 95 | 20 | – | 23 | |
| Alloy | Temper | UTS(Mpa) | % Elongation | |||
| Min | Max | 0.5 mm -0.8 mm | 0.81 mm - 1.30 mm | 1.30 mm - above | ||
| 1060 | O | 55 | 75 | 25 | 25 | 30 |
| H12 | 75 | 110 | 6 | 6 | 7 | |
| H14 | 90 | 120 | 5 | 5 | 6 | |
| H16 | 95 | 130 | 4 | 4 | 4 | |
| H18 | 130 | --- | 3 | 3 | 3 | |
| Properties | Conditions | ||
| T (°C) | Treatment | ||
| Density (×1000 kg/m3) | 7.7-8.03 | 25 | |
| Poisson's Ratio | 0.27-0.30 | 25 | |
| Elastic Modulus (GPa) | 190-210 | 25 | |
| Tensile Strength (Mpa) | 640 | 25 | cold drawn, spheroidized annealed more |
| Yield Strength (Mpa) | 495 | ||
| Elongation (%) | 10 | ||
| Reduction in Area (%) | 45 | ||
| Hardness (HB) | 192 | 25 | cold drawn, spheroidized annealed more |
| Alloy | Temper | UTS(Mpa) | % Elongation | |||
| Min | Max | 0.5 mm -0.8 mm | 0.81 mm - 1.30 mm | 1.30 mm - above | ||
| 1100 | O | 75 | 110 | 20 | 25 | 29 |
| H12 | 95 | 130 | 5 | 6 | 7 | |
| H14 | 110 | 145 | 3 | 4 | 5 | |
| H16 | 130 | 165 | 2 | 3 | 4 | |
| H18 | 150 | --- | 2 | 2 | 3 | |
| Alloy | Temper | UTS (Mpa) | Yield Strength (Mpa) | Elongation (%) | ||
| - | - | Minimum | Maximum | Minimum | Maximum | A 50mm (Minimum) |
| EN AW-2014 | O | – | 250 | – | 135 | 10 |
| T4 | 370 | – | 230 | – | 11 | |
| Material | Tensile Strength (N/mm²) min | Yield Strength | Elongation in 4D % | ||
| ksi | Mpa | ksi | Mpa | ||
| Aluminum 2017 | 55 | 379 | 32 | 221 | 12 |
| Temper | Tensile Strength | Yield Strength | Elongation |
| KSI | KSI | % | |
| (annealed) | 32 | 14 | 12 |
| T3 | 63 | 42 | 15 |
| Properties | Metric | Imperial |
| Tensile strength | 130 MPa | 18855 psi |
| Yield strength | 125 MPa | 18130 psi |
| Shear strength | 83 MPa | 12039 psi |
| Fatigue strength | 55 MPa | 7977 psi |
| Elastic modulus | 70-80 GPa | 10153-11603 ksi |
| Poisson's ratio | 0.33 | 0.33 |
| Elongation | 10% | 10% |
| Hardness | 35 | 35 |
| Temper | 0.2% Proof Stress, MPa min† | Tensile Strength, MPa | Elongation % min‡ |
| O (annealed) | 35 | 105 – 145 | 12 – 22 |
| H12 | 95 | 125 – 165 | 2 – 8 |
| H14 | 115 | 145 – 185 | 1 – 6 |
| H16 | 135 | 165 – 205 | 1 – 3 |
| H18 | – | > 185 | 1 – 3 |
| H32 | 85 | 115 – 160 | 3 – 9 |
| H34 | 105 | 135 – 180 | 2 – 7 |
| H36 | 125 | 160 – 200 | 1 – 4 |
| H38 | – | > 180 | 1 – 4 |
| Hardness, Brinell | Poisson's Ratio | Melting Point | Electrical Resistivity | Modulus of Elasticity | Specific Heat |
| 47 | 0.33 | 607 - 649 °C | 4.99e-006 ohm-cm | 70.3 GPa | 0.88 J/g-°C |
| Proof Stress | Tensile Strength | Elongation at 50 mm | Hardness Brinell |
| 80 Min MPa | 190 - 260MPa | 12 Min % | 52 HB |
| Proof Stress | Tensile Strength | Hardness Brinell | Elongation |
| 125 Min MPa | 275 - 350 MPa | 75 HB | 12 Min % |
| Proof Stress | Tensile Strength | Hardness Brinell | Elongation |
| 125 Min MPa | 275 - 350 MPa | 75 HB | 12 Min % |
| Tensile Strengtd (PSI) | Yield Strengtd (PSI) | Shear Strengtd (PSI) | Elongation in 2″ | Brinell Hardness |
| 45,000 | 40,000 | 31,000 | 12 | 95 |
| Tensile Strength, MPa | Yield Strength 0.2%, MPa | Elongation % | Hardness HBW |
| 295 | 240 | 8 | 95 |
| Material | Temper | Tensile Strength (ksi) | Yield Strength (ksi) | Elongation in 2" % |
| Aluminium Alloy 7050 Angle (AMS 4340) | T76511 | 79 | 69 | 7 |
| Aluminium Alloy 7050 Angle (AMS 4340) | T73511 | 70 | 60 | 8 |
| Aluminium Alloy 7050 Angle (AMS 4342) | T74511 | 73 | 63 | 7 |
| Temper | Tensile | Hardness | ||||
| Ultimate | Yield | Elongation | Brinell | |||
| KSI | MPA | KSI | MPA | % | ||
| T6, T651 | 83 | 572 | 73 | 503 | 11 | 150 |
| T73, T7351 | 73 | 503 | 63 | 434 | 13 | N/A |
| Alloy | Temper | UTS (Mpa) | Yield Strength (Mpa) | Elongation (%) | ||
|---|---|---|---|---|---|---|
| - | - | Minimum | Maximum | Minimum | Maximum | A 50mm (Minimum) |
| EN AW-2014 | O | – | 250 | – | 135 | 10 |
| T4 | 370 | – | 230 | – | 11 | |
| Alloy | Temper | Tensile Strength (N/mm²) min | Yield Strength (Mpa) | Elongation in 4D % | ||
|---|---|---|---|---|---|---|
| T6 | ksi | Mpa | ksi | Mpa | A 50mm (Minimum) | |
| 2017 | T651 | 60 | – | 20 | – | 23 |
| T6511 | 60 | 95 | 20 | – | 23 | |
| Temper | Tensile Strength | Yield Strength | Elongation |
| T6 | KSI | KSI | % |
| T65 | 32 | 14 | 12 |
| T651 | 63 | 42 | 15 |
| Proof Stress | Tensile Strength | Hardness Brinell | Elongation |
| 125 Min MPa | 275 - 350 MPa | 75 HB | 12 Min % |
| Tensile Strengtd (PSI) | Yield Strengtd (PSI) | Shear Strengtd (PSI) | Elongation in 2″ | Brinell Hardness |
| 45,000 | 40,000 | 31,000 | 12 | 95 |
| Tensile Strength (psi) | Yield Strength (psi) | Elongation (% in 2") | Brinell Hardness |
| 27,000 | 21,000 | 12 | 60 |
| Material | Diameter (mm) | Tensile Strength min (N/mm²) | Yield Strength min (N/mm²) | Elongation on 5.65v % (min) |
| Alloy 6082 | < 20 | 295 | 255 | 8 |
| 20 - 150 | 310 | 270 | 8 | |
| 150 - 200 | 280 | 240 | 5 |
| Standard | Temper | Tensile | Hardness | ||||
| Aluminium 7075 | Ultimate | Yield | Elongation | Brinell | |||
| T6, T651, T6511 | KSI | MPA | KSI | MPA | % | ||
| 83 | 572 | 73 | 503 | 11 | 150 | ||
| 73 | 503 | 63 | 434 | 13 | N/A | ||
| Material | Temper | Diameter (mm) | Tensile Strength min ((N/mm²) | Yield Strength (min) (N/mm²) | Elongation on 5.65 V (min) |
| 2014 Bar | T4 | <20 | 370 | 230 | 11 |
| 2014 Bar | T4 | 20-75 | 390 | 250 | 11 |
| 2014 Bar | T4 | 75-150 | 390 | 250 | 9 |
| 2014 Bar | T4 | 150-200 | 370 | 230 | 8 |
| 2014 Bar | T6510 | 20-75 | 480 | 435 | 7 |
| 2014 Bar | T6510 | 75-150 | 465 | 420 | 7 |
| 2014 Bar | T6510 | 150-200 | 435 | 390 | 7 |
| Material | Condition | Tensile Strength (N/mm²) min | Yield Strength | Elongation in 4D % | ||
| ksi | Mpa | ksi | Mpa | |||
| 2017 | 2017-T4 Bar | 55 | 379 | 32 | 221 | 12 |
| Temper | Tensile Strength | Yield Strength | Elongation |
| KSI | KSI | % | |
| (annealed) | 32 | 14 | 12 |
| T3 | 63 | 42 | 15 |
| Properties | Proof Stress | Tensile Strength | Hardness Brinell | Elongation |
| Metric | 125 Min MPa | 275 - 350 MPa | 75 HB | 12 Min % |
| Tensile Strengtd (PSI) | Yield Strengtd (PSI) | Shear Strengtd (PSI) | Elongation in 2″ | Brinell Hardness |
| 45,000 | 40,000 | 31,000 | 12 | 95 |
| Tensile Strength (psi) | Yield Strength (psi) | Elongation (% in 2") | Brinell Hardness |
| 27,000 | 21,000 | 12 | 60 |
| Diameter or minor sectional dimension mm | Tensile Strength, MPa | Yield Strength 0.2%, MPa | Elongation % |
| 0-20 | 295 | 255 | 8 |
| 20-150 | 310 | 270 | 8 |
| 150-200 | 280 | 240 | 5 |
| Temper | Tensile | Hardness | ||||
| Ultimate | Yield | Elongation | Brinell | |||
| KSI | MPA | KSI | MPA | % | ||
| T6, T651 | 83 | 572 | 73 | 503 | 11 | 150 |
| T73, T7351 | 73 | 503 | 63 | 434 | 13 | N/A |
| Material | Temper | Diameter (mm) | Tensile Strength min ((N/mm²) | Yield Strength (min) (N/mm²) | Elongation on 5.65 V (min) |
| 2014 Pipes | T4 | <20 | 370 | 230 | 11 |
| 2014 Pipes | T4 | 20-75 | 390 | 250 | 11 |
| 2014 Pipes | T4 | 75-150 | 390 | 250 | 9 |
| 2014 Pipes | T4 | 150-200 | 370 | 230 | 8 |
| 2014 Pipes | T6510 | 20-75 | 480 | 435 | 7 |
| 2014 Pipes | T6510 | 75-150 | 465 | 420 | 7 |
| Temper | Tensile Strength | Yield Strength | Elongation |
| KSI | KSI | % | |
| (annealed) | 32 | 14 | 12 |
| T3 | 63 | 42 | 15 |
| Properties | Proof Stress | Tensile Strength | Hardness Brinell | Elongation |
| Metric | 125 Min MPa | 275 - 350 MPa | 75 HB | 12 Min % |
| Tensile Strength (PSI) | Yield Strengtd (PSI) | Shear Strengtd (PSI) | Elongation in 2″ | Brinell Hardness |
| 45,000 | 40,000 | 31,000 | 12 | 95 |
| Tensile Strength (psi) | Yield Strength (psi) | Elongation (% in 2") | Brinell Hardness |
| 27,000 | 21,000 | 12 | 60 |
| Diameter or minor sectional dimension mm | Tensile Strength, MPa | Yield Strength 0.2%, MPa | Elongation % |
| 0-20 | 295 | 255 | 8 |
| 20-150 | 310 | 270 | 8 |
| 150-200 | 280 | 240 | 5 |